Celanese Corporation塞拉尼斯PA, 玻璃纤维增强材料

 

Celstran® PA66-GF40-0101P10/11

聚酰胺 66/6 共聚物

Celanese Corporation

Technical Data

 

产品说明

PA66/6 Copolymer with 40% ash content

Material code according to ISO 1043-1: PA66 Nylon 66/6 Copolymer reinforced by 40 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.

总览

材料状态 • 已商用：当前有效

搜索 UL 黄卡 •  Celanese Corporation

•  Celstran®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

填料/增强材料 • 玻璃纤维增强材料

形式 • 粒子

加工方法 • 注射成型

多点数据 • Specific Volume vs Temperature (ISO 11403-2)

物理性能 干燥 调节后的 单位制 测试方法

密度 1.46 -- g/cm³ ISO 1183

吸水率 (饱和, 23°C) 1.2 -- % ISO 62

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量 12800 9000 MPa ISO 527-1/1A

拉伸应力 (断裂) 240 165 MPa ISO 527-2/1A/5

拉伸应变 (断裂) 2.3 2.7 % ISO 527-2/1A/5

弯曲模量 ISO 178

23°C 11500 8300 MPa

80°C 8300 -- MPa

弯曲应力 ISO 178

23°C 350 270 MPa

80°C 240 -- MPa

Flexural Strain at Flexural Strength (80°C) 4.0 0.0 % ISO 178

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 ISO 179/1eA

-30°C 42 -- kJ/m²

23°C 40 35 kJ/m²

简支梁无缺口冲击强度 ISO 179/1eU

-30°C 75 -- kJ/m²

23°C 80 110 kJ/m²

无缺口伊佐德冲击强度 ISO 180/1U

-30°C 65 -- kJ/m²

23°C 72 -- kJ/m²

热性能 干燥 调节后的 单位制 测试方法

热变形温度

1.8 MPa, 未退火 235 -- °C ISO 75-2/A

8.0 MPa, 未退火 220 -- °C ISO 75-2/C

熔融温度 2 240 -- °C ISO 11357-3

注射 干燥单位制

干燥温度 70 到 80°C

干燥时间 2.0 到 4.0hr

 

Celstran® PA66-GF40-0101P10/11

聚酰胺 66/6 共聚物

 

Celanese Corporation

注射 干燥单位制

建议的最大水分含量 0.15%

料斗温度 70 到 80°C

Injection Feed Temperature 20 到 50°C

料筒后部温度 280 到 285°C

料筒中部温度 280 到 290°C

料筒前部温度 290 到 300°C

Injection Zone 4 Temperature 300 到 310°C

射嘴温度 310 到 320°C

加工（熔体）温度 310°C

模具温度 90 到 120°C

注射速度 中等

背压 < 3.00MPa

Hot Runner 300 到 315°C

Screw Speed

4.00 cm 50

5.50 cm 35

7.50 cm 25

 

 

 

 

塞拉尼斯聚酰胺 66/6 共聚物PA66+PA6,塞拉尼斯PA66+PA6 Celstran® PA66-GF40-0101P10/11是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123   13549213581 肖生    QQ：15397858   微信：13549213581